85micron Clear PE film/ Acrylic adhesive/ White glassine liner

Price:

Product number:D40

Category: Hose Label

隐藏域元素占位

Description

Application

•Minimum labeling temp: 0℃. Service temp: -30℃~70C. (24h after labeling).

•Suitable for daily chemical, personal care, medicine and other fields: such as bottle label, sealing label etc.

•Due to the stiffer facestock, this material is not recommended for bottles with diameter less than 20mm or labeling to irregular curved surfaces or very soft bottle.

•Not recommended to use in repeated stick occasion.

•Suitable for film "no-label look" transparent label.

Print & Process

•Can be used in multiple printing methods such as letterpress, flexo, gravure, and screen printing etc.

•UV ink & water-based ink is suitable.

•Control the viscosity of print ink, high-contractility bring label crimp, cause the label detach fromrelease paper or warp from label object.

•Film special die-cutting knife is recommended, especially the flat die-cutting.

Facestock

A kind of transparent PE film, being corona treated, have good printability.

Indicator	Parameter	Unit	Method
Basic Weight	78±5%	g/m²	ISO 536
Caliper	85±5%	μm	TAPPI T-411
Haze	≤3	%	ASTM D1003

Adhesive

General purpose membrane emulsion acrylic adhesive.

Liner

Super calendered white glassine.

Indicator	Parameter	Unit	Method
Basic Weight	60±5%	g/㎡	ISO 536
Caliper	53±5%	μm	ISO 534
Tensile Strength	≥300	mN	ISO 1924

Performance data

Indicator	Parameter	Unit	Method
Initial Tack	≥8	N/25mm	FTM9，ss
90°Peel Adhesion(20min)	≥5	N/25mm	FTM2，ss
Shear Min.	≥15	hours	FTM8，ss

Shelf life

From date of manufacture 12 months, storage conditions: 23±2℃ & relative humidity 50±5%.Prolonged storage outside these conditions might reduce the shelf life

Statement

•All the statements, tech information & recommendations are based on the tests believed to be reliable but do not constitute a guarantee or warranty.

•All products are sold with the understanding that purchaser has independently determined the suitability of such products for its purposes.

•We reserve the rights of final explanation.

Keywords: